Crystal laminate structure and method for producing same

ABSTRACT

A crystal laminate structure, in which crystals can be epitaxially grown on a β-Ga 2 O 3 -based substrate with high efficiency to produce a high-quality β-Ga 2 O 3 -based crystal film on the substrate; and a method for producing the crystal laminate structure are provided. The crystal laminate structure includes: a β-Ga 2 O 3 -based substrate, of which the major face is a face that is rotated by 50 to 90° inclusive with respect to face; and a β-Ga 2 O 3 -based crystal film which is formed by the epitaxial crystal growth on the major face of the β-Ga 2 O 3 -based substrate.

TECHNICAL FIELD

The invention relates to a crystal laminate structure (or laminated crystal structure) and a method for producing the crystal laminate structure and, in particular, to a crystal laminate structure including a β-Ga₂O₃-based substrate with a β-Ga₂O₃-based crystal film and a method for producing the crystal laminate structure.

BACKGROUND ART

A conventional semiconductor element in which a Ga-containing oxide is deposited on an element substrate formed of a β-Ga₂O₃ single crystal is known (see, e.g., PTL 1).

This type of semiconductor element is formed by laminating a layer(s) of n-type or p-type conductivity on a main surface of a β-Ga₂O₃ single crystal substrate using a physical vapor-phase growth method such as MBE (Molecular Beam Epitaxy) or a chemical vapor-phase growth method such as CVD.

In addition, a (100) plane having high cleavability and thus providing a flat surface easily is often used as the main surface of the β-Ga₂O₃ single crystal substrate (see, e.g., PTL 2).

CITATION LIST Patent Literature

[PTL 1]

-   JP-A-2005-235961     [PTL 2] -   JP-A-2008-156141

SUMMARY OF INVENTION Technical Problem

In general, growth temperature needs to be high to some extent in order that high-quality crystals without mixture of heterogeneous phase are formed by epitaxial growth. However, when a crystal is epitaxially grown on a β-Ga₂O₃ single crystal substrate having a (100) plane as a main surface, a growth rate tends to decrease with increasing growth temperature of the crystal. It is believed that this is because raw materials of the crystal re-evaporate from the substrate and this causes a problem that the raw materials are wasted.

It is an object of the invention to provide a crystal laminate structure that crystals can be epitaxially grown on a β-Ga₂O₃-based substrate with high efficiency to produce a high-quality β-Ga₂O₃-based crystal film, and a method for producing the crystal laminate structure.

Solution to Problem

According to one embodiment of the invention, a crystal laminate structure as defined in [1] to [3] below and a method for producing a crystal laminate structure as defined in [4] to [6] below are provided so as to achieve the above object.

[1] A crystal laminate structure, comprising:

-   -   a β-Ga₂O₃-based substrate comprising as a main surface a plane         rotated by not less than 50° and not more than 90° with respect         to a (100) plane; and     -   a β-Ga₂O₃-based crystal film that is formed by epitaxially         growing a crystal on the main surface of the β-Ga₂O₃-based         substrate.

[2] The crystal laminate structure according to [1], wherein the main surface comprises one of a (010) plane, a (001) plane, a (−201) plane, a (101) plane and a (310) plane.

[3] The crystal laminate structure according to [1] or [2], wherein the β-Ga₂O₃-based crystal film comprises a (Al_(1-x)Ga_(x))₂O₃ crystal (0<x≦1).

[4] A method for producing a crystal laminate structure, comprising:

-   -   a step of forming a β-Ga₂O₃-based crystal film by epitaxial         growth of a β-Ga₂O₃-based crystal on a main surface of a         β-Ga₂O₃-based substrate,

wherein the main surface comprises a plane rotated by not less than 50° and not more than 90° with respect a (100) plane.

[5] The method for producing a crystal laminate structure according to [4], wherein the main surface comprises one of a (010) plane, a (001) plane, a (−201) plane, a (101) plane and a (310) plane.

[6] The method for producing a crystal laminate structure according to [4] or [5], wherein a growth temperature for the epitaxial growth is not less than 700° C.

Advantageous Effects of Invention

According to an embodiment of the invention, a crystal laminate structure can be provided that crystals can be epitaxially grown on a β-Ga₂O₃-based substrate with high efficiency to produce a high-quality β-Ga₂O₃-based crystal film, as well as a method for producing the crystal laminate structure.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a cross sectional view showing a crystal laminate structure in a first embodiment.

FIG. 2 is a cross sectional view showing an MBE system used for forming the crystal laminate structure.

FIG. 3 is a cross sectional view showing a high-electron-mobility transistor in a second embodiment.

FIG. 4 is a cross sectional view showing a MESFET in a third embodiment.

FIG. 5 is a cross sectional view showing a Schottky-barrier diode in a fourth embodiment.

FIG. 6 is a graph showing the growth rate ofβ-Ga₂O₃ crystal onβ-Ga₂O₃ single crystal substrates.

FIG. 7 is a graph showing a relation between the growth rate of β-Ga₂O₃ crystal and a rotation angle with respect to a (100) plane as a main surface of the β-Ga₂O₃ single crystal substrate.

DESCRIPTION OF EMBODIMENTS

[First Embodiment]

According to the present embodiment, β-Ga₂O₃-based crystals can be epitaxially grown on a β-Ga₂O₃-based substrate with high efficiency to form a high-quality β-Ga₂O₃-based crystal film without mixture of heterogeneous phase. In conventional methods in which a β-Ga₂O₃-based crystal is epitaxially grown on a β-Ga₂O₃-based substrate having a (100) plane as a main surface, a sufficient growth rate is not obtained at a growth temperature required to grow high-quality crystals, e.g., at a growth temperature of not less than 700° C., and it is not possible to efficiently grow crystals. However, the present inventors found that, when a β-Ga₂O₃-based substrate of which main face is a plane rotated by not less than 50° and not more than 90° with respect a (100) plane is used as a base for epitaxial crystal growth, high-quality β-Ga₂O₃-based crystals are grown at a sufficient rate. Examples of embodiments thereof will be described in detail below.

(Configuration of Crystal Laminate Structure)

FIG. 1 is a cross sectional view showing a crystal laminate structure in the first embodiment. A crystal laminate structure 2 includes a β-Ga₂O₃-based substrate 1 and a β-Ga₂O₃-based crystal film 20 formed on a main surface 10 of the β-Ga₂O₃-based substrate 1.

The main surface 10 of the β-Ga₂O₃-based substrate 1 is a plane which is rotated by not less than 50° and not more than 90° with respect the (100) plane. In other words, in the β-Ga₂O₃-based substrate 1, an angle θ (0<θ≦90°) formed between the main surface 10 and the (100) plane is not less than 50°. Examples of the plane rotated by not less than 50° and not more than 90° with respect the (100) plane include a (010) plane, a (001) plane, a (−201) plane, a (101) plane and a (310) plane.

When the main surface 10 of the β-Ga₂O₃-based substrate 1 is a plane rotated by not less than 50° and not more than 90° with respect the (100) plane, it is possible to effectively suppress re-evaporation of raw materials of the β-Ga₂O₃-based crystal from the β-Ga₂O₃-based substrate 1 at the time of epitaxially growing the β-Ga₂O₃-based crystal on the β-Ga₂O₃-based substrate 1. In detail, where a percentage of the re-evaporated raw material during growth of the β-Ga₂O₃-based crystal at a growth temperature of 500° C. is defined as 0%, the percentage of the re-evaporated raw material can be suppressed to be not more than 40% when the main surface 10 of the β-Ga₂O₃-based substrate 1 is a plane rotated by not less than 50° and not more than 90° with respect the (100) plane. It is thus possible to use not less than 60% of the supplied raw material to form the β-Ga₂O₃-based crystal, which is preferable from the viewpoint of growth rate and manufacturing cost of the β-Ga₂O₃-based crystal.

The β-Ga₂O₃-based substrate 1 is formed of, e.g., a β-Ga₂O₃ single crystal. The β-Ga₂O₃ crystal has a monoclinic crystal structure and typically has lattice constants of a=12.23 Å, b=3.04 Å, c=5.80 Å, α=γ=90° and β=103.7°.

In the β-Ga₂O₃ crystal, the (100) plane comes to coincide with the (310) plane when rotated by 52.5° around the c-axis and comes to coincide with the (010) plane when rotated by 90°. Meanwhile, the (100) plane comes to coincide with the (101) plane when rotated by 53.8° around the b-axis, comes to coincide with the (001) plane when rotated by 76.3° and comes to coincide with the (−201) plane when rotated by 53.8°.

It should be noted that, the β-Ga₂O₃-based substrate 1 is basically formed of a β-Ga₂O₃ single crystal as described above but may be foamed of an oxide including mainly Ga doped with one or more elements selected from the group consisting of Cu, Ag, Zn, Cd, Al, In, Si, Ge and Sn. It is possible to control a lattice constant, bandgap energy or electrical conduction properties by adding such elements. It is possible to use the β-Ga₂O₃-based substrate 1 formed of, e.g., a (Ga_(x)Al_(y)In_((1-x-y)))₂O₃ (where 0<x≦1, 0≦y≦1, 0<x+y≦) crystal which is a β-Ga₂O₃ crystal doped with Al and In. The band gap is widened by adding Al and is narrowed by adding In.

When the elements listed above are added to the β-Ga₂O₃ crystal, lattice constants may slightly change. Even in such a case, the (010) plane, the (001) plane, the (−201) plane, the (101) plane and the (310) plane still fall under the category of a plane rotated by not less than 50° and not more than 90° with respect the (100) plane.

The β-Ga₂O₃-based crystal film 20 is formed of a β-(Al_(1-x)Ga_(x))₂O₃ crystal (0<x≦1), e.g., a β-Ga₂O₃ crystal (when x=1). In addition, the β-Ga₂O₃-based crystal film 20 may contain conductive impurities.

(Method for Producing Crystal Laminate Structure)

Firstly, an ingot for forming the β-Ga₂O₃-based substrate 1 is produced by, e.g., the FZ (Floating Zone) method or the EFG (Edge Defined Film Fed Growth) method, etc.

In case of using the FZ method, an ingot is formed using, e.g., an infrared-heating single crystal manufacturing system. In detail, firstly, an end of a seed crystal is held on a seed chuck and an upper end portion of a rod-like polycrystalline raw material is held on a raw-material chuck. After adjusting a vertical position of an upper rotating shaft, the top edge of the seed crystal is brought into contact with the lower edge of the polycrystalline raw material. The vertical position of the upper rotating shaft and that of a lower rotating shaft are adjusted so that light of halogen lamp is focused on the upper edge of the seed crystal and the lower edge of the polycrystalline raw material. After the adjustment, the upper edge of the seed crystal and the lower edge of the polycrystalline raw material are heated so that the heated portion is melted, thereby forming melt droplets. At this time, only the seed crystal is being rotated. The aforementioned portion is melted while rotating the polycrystalline raw material and the seed crystal in opposite directions so as to be mixed sufficiently and the polycrystalline raw material and the seed crystal are then pulled in directions opposite to each other to form a single crystal having appropriate length and thickness, thereby making an ingot.

In case of using the EFG method, a predetermined amount ofβ-Ga₂O₃ powders, etc., to be a raw material is put in a crucible and is melted by heating, thereby producing β-Ga₂O₃ melt. Through a slit formed on a slit die which is placed in the crucible, the β-Ga₂O₃ melt is drawn up to an upper surface of the slit die by capillary action, the β-Ga₂O₃ melt is cooled by contact with the seed crystal and an ingot having an arbitrary cross sectional shape is thereby formed.

It should be noted that, a desired conductive impurity may be added when producing β-Ga₂O₃ ingots by such producing methods.

The β-Ga₂O₃ ingot formed as described above is sliced by, e.g., a wire saw so that a cross section thereof is a plane rotated by not less than 50° and not more than 90° with respect the (100) plane, thereby obtaining the β-Ga₂O₃-based substrate 1 having a thickness of 1 mm In the subsequent grinding and polishing process, the β-Ga₂O₃-based substrate 1 is ground and polished until the thickness becomes about 600 μm.

Next, the β-Ga₂O₃-based substrate 1 is subjected to organic cleaning using methanol, acetone and methanol in this order for three minutes each, running water cleaning using ultrapure water, hydrofluoric acid immersion cleaning for fifteen minutes, sulfuric acid/hydrogen peroxide mixture immersion cleaning for five minutes and running water cleaning using ultrapure water, and is further subjected to thermal cleaning under conditions of at 800° C. for ten minutes. After this, the main surface 10 of the β-Ga₂O₃-based substrate 1 is ready for epitaxial growth of the β-Ga₂O₃-based crystal film 20.

The method of forming the β-Ga₂O₃-based crystal film 20 on the main surface 10 of the β-Ga₂O₃-based substrate 1 is PLD (Pulsed Laser Deposition), CVD (Chemical Vapor Deposition), sputtering and MBE (Molecular Beam Epitaxy) etc. In the present embodiment, a process using the MBE will be described as an example.

The MBE is a crystal growth method in which a single or compound solid is heated in an evaporation source called cell and vapor generated by heat is supplied as a molecular beam onto the surface of the substrate.

FIG. 2 is a cross sectional view showing an MBE system used for forming the crystal laminate structure 2. The MBE system 3 is provided with a vacuum chamber 30, a substrate holder 31 supported in the vacuum chamber 30 to hold the β-Ga₂O₃-based substrate 1, heating devices 32 held on the substrate holder 31, plural cells 33 (33 a, 33 b, 33 c, 33 d) each containing one of raw materials of the β-Ga₂O₃-based crystal film 20, heaters 34 (34 a, 34 b, 34 c, 34 d) for respectively hearing the plural cells 33, a gas supply pipe 35 for supplying oxygen gas into the vacuum chamber 30, and a vacuum pump 36 for exhausting the air in the vacuum chamber 30. It is configured that the substrate holder 31 can be rotated by a non-illustrated motor via a shaft 310.

A Ga raw material and an Al raw material are respectively loaded in the first cell 33 a and the second cell 33 b. An n-type impurity raw material to be doped as a donor, such as Si or Sn, is loaded in the third cell 33 c. A p-type impurity raw material to be doped as an acceptor, such as Mg or Zn, is loaded in the fourth cell 33 d. Each of the first to fourth cells 33 a to 33 d is provided with a non-illustrated shutter and is configured such that the shutter can be closed when the raw material contained therein is not used.

Firstly, the β-Ga₂O₃-based substrate 1 is attached to the substrate holder 31 of the MBE system 3. Next, the vacuum pump 36 is activated to reduce atmospheric pressure in the vacuum chamber 30 to about 10⁻¹⁰ Ton. Then, the β-Ga₂O₃-based substrate 1 is heated by the heating devices 32. It should be noted that, radiation heat of heat source such as graphite heater of the heating device 32 is thermally transferred to the β-Ga₂O₃-based substrate 1 via the substrate holder 31 and the β-Ga₂O₃-based substrate 1 is thereby heated.

After the β-Ga₂O₃-based substrate 1 is heated to a predetermined temperature, oxygen-based gas is supplied into the vacuum chamber 30 through the gas supply pipe 35.

After a period of time required for stabilization of gas pressure in the vacuum chamber 30 (e.g., after 5 minutes) since the oxygen-based gas was supplied into the vacuum chamber 30, the cells 33 a and 33 b are heated by the heaters 34 a and 34 b while rotating the substrate holder 31 so that Ga vapor and Al vapor are started to be supplied. In case that a Ga₂O₃ crystal film not containing Al is formed as the β-Ga₂O₃-based crystal film 20, the first cell 33 a is heated to start supply of Ga vapor.

Meanwhile, when imparting an n-type conductivity to the β-Ga₂O₃-based crystal film 20, vapor of the n-type impurity to be a donor such as Si or Sn is supplied from the third cell 33 c by heating the third heater 34 c. On the other hand, when imparting a p-type conductivity, vapor of the p-type impurity to be an acceptor such as Mg or Zn is supplied from the fourth cell 33 d by heating the fourth heater 34 d.

The vapor produced from each cell 33 is radiated as molecular beam onto the surface of the β-Ga₂O₃-based substrate 1. Beam-equivalent pressure (BEP) of Ga and that of Al are, e.g., respectively 1.5×10⁻⁵ Pa and 5×10⁻⁷ Pa. Meanwhile, in case of not producing Al vapor, for example, the Ga beam-equivalent pressure is e.g., 3×10⁻⁵ Pa.

Then, a β-Ga₂O₃-based crystal is epitaxially grown on the main surface 10 of the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 is thereby formed. Growth temperature and growth time of the β-Ga₂O₃-based crystal are, e.g., respectively 700° C. and 1 hour.

In addition, the β-Ga₂O₃-based crystal film 20 may be subjected to annealing treatment in an inert atmosphere, where necessary. The annealing treatment is performed in a heat treatment equipment such as lamp annealing apparatus. Alternatively, the annealing treatment may be performed in the MBE system 1.

[Second Embodiment]

A high-electron-mobility transistor (HEMT), which is one of semiconductor devices including the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 of the first embodiment, will be described as the second embodiment.

FIG. 3 is a cross sectional view showing a high-electron-mobility transistor in the second embodiment. This high-electron-mobility transistor 4 includes the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 of the first embodiment. The high-electron-mobility transistor 4 further includes an n-type β-(AlGa)₂O₃ layer 41 on the β-Ga₂O₃-based crystal film 20, and a gate electrode 42, a source electrode 43 and a drain electrode 44 on the n-type β-(AlGa)₂O₃ layer 41. The gate electrode 42 is arranged between the source electrode 43 and the drain electrode 44.

The gate electrode 42 is in contact with a surface 41 a of the n-type β-(AlGa)₂O₃ layer 41, thereby forming a Schottky junction. Meanwhile, the source electrode 43 and the drain electrode 44 are in contact with the surface 41 a of the n-type β-(AlGa)₂O₃ layer 41, thereby faulting an ohmic junction.

In the second embodiment, the β-Ga₂O₃-based substrate 1 contains group II elements such as Mg and has high electrical resistance.

In the present embodiment, the β-Ga₂O₃-based crystal film 20 is of an i-type and functions as an electron transit layer. This i-typeβ-Ga₂O₃-based crystal film 20 is formed by epitaxially growing a β-Ga₂O₃-based single crystal on the main surface 10 of the β-Ga₂O₃-based substrate 1.

The n-type β-(AlGa)₂O₃ layer 41 is an electron supply layer doped with a donor such as Si or Sn and is formed by epitaxial growth on the β-Ga₂O₃-based crystal film 20.

Since the β-Ga₂O₃-based crystal film 20 and the n-type β-(AlGa)₂O₃ layer 41 have different band gaps, discontinuity of bands occurs at the interface therebetween, electrons generated from the donor in the n-type β-(AlGa)₂O₃ layer 41 are concentrated on the β-Ga₂O₃-based crystal film 20 side and are distributed in a region in the vicinity of the interface, and an electron layer called two-dimensional electron gas is thereby formed.

As such, a first depletion layer due to the Schottky junction with the gate electrode 42 and a second depletion layer due to the formation of two-dimensional electron gas are produced in the n-type β-(AlGa)₂O₃ layer 41. The n-type β-(AlGa)₂O₃ layer 41 has a thickness at which the first depletion layer is in contact with the second depletion layer.

Voltage is applied to the gate electrode 42 to change the thicknesses of the first and second depletion layers and to adjust the concentration of the two-dimensional electron gas, thereby allowing drain current to be controlled.

The thickness of the β-Ga₂O₃-based crystal film 20 is not specifically limited but is desirably not less than 0.1 nm. In addition, the thickness of the n-type β-(AlGa)₂O₃ layer 41 is set to 0.1 to 10 μm depending on a doping concentration.

[Third Embodiment]

A MESFET (Metal-Semiconductor Field Effect Transistor), which is one of semiconductor devices including the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 of the first embodiment, will be described as the third embodiment.

FIG. 4 is a cross sectional view showing a MESFET in the third embodiment. This MESFET 5 includes the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 of the first embodiment. The MESFET 5 further includes a gate electrode 52, a source electrode 53 and a drain electrode 54 on the β-Ga₂O₃-based crystal film 20. The gate electrode 52 is arranged between the source electrode 53 and the drain electrode 54.

The gate electrode 42 is in contact with a surface 21 a of the β-Ga₂O₃-based crystal film 20, thereby forming a Schottky junction. Meanwhile, the source electrode 53 and the drain electrode 54 are in contact with the surface 21 a of the β-Ga₂O₃-based crystal film 20, thereby forming an ohmic junction.

In the third embodiment, the β-Ga₂O₃-based substrate 1 contains group II elements such as Mg and has high electrical resistance.

In the present embodiment, the β-Ga₂O₃-based crystal film 20 is of an n-type and the donor concentration thereof in the vicinity of contact areas with the source electrode 53 and with the drain electrode 54 is higher than that in the remaining portion.

The thickness of the depletion layer in the β-Ga₂O₃-based crystal film 20 under the gate electrode 52 is changed by controlling bias voltage applied to the gate electrode 52, thereby allowing drain current to be controlled.

[Fourth Embodiment]

A Schottky-barrier diode, which is one of semiconductor devices including the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 of the first embodiment, will be described as the fourth embodiment.

FIG. 5 is a cross sectional view showing a Schottky-barrier diode in the fourth embodiment. This Schottky-barrier diode 6 includes the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 of the first embodiment. The Schottky-barrier diode 6 further includes a Schottky electrode 62 on the β-Ga₂O₃-based crystal film 20 and an ohmic electrode 63 on a surface 11 of the β-Ga₂O₃-based substrate 1 opposite to the β-Ga₂O₃-based crystal film 20.

The Schottky electrode 62 is in contact with the surface 21 a of the β-Ga₂O₃-based crystal film 20, thereby forming a Schottky junction. Meanwhile, the ohmic electrode 63 is in contact with the surface 11 of the β-Ga₂O₃-based substrate 1, thereby forming an ohmic junction.

In the fourth embodiment, the β-Ga₂O₃-based substrate 1 and the β-Ga₂O₃-based crystal film 20 are of an n-type and the donor concentration of the β-Ga₂O₃-based crystal film 20 is lower than that of the β-Ga₂O₃-based substrate 1.

When forward voltage (electric potential is positive on the Schottky electrode 62 side) is applied to the Schottky diode 6, the number of electrons moving from the β-Ga₂O₃-based substrate 1 to the β-Ga₂O₃-based crystal film 20 is increased. As a result, a forward current flows from the Schottky electrode 62 to the ohmic electrode 63.

On the other hand, when reverse voltage (electric potential is negative on the Schottky electrode layer 62 side) is applied to the Schottky diode 6, substantially no electric current flows through the Schottky diode 6.

(Effects of the Embodiments)

According to the embodiments described above, since a β-Ga₂O₃-based substrate of which main face is a plane rotated by not less than 50° and not more than 90° with respect the (100) plane is used as a base for epitaxial crystal growth, it is possible to grow a β-Ga₂O₃-based crystal at a sufficient rate and thereby to form a high-quality β-Ga₂O₃-based crystal film. In addition, use of such high-quality β-Ga₂O₃-based crystal films allows high-performance semiconductor devices excellent in operating characteristics to be formed.

In addition, since waste of the raw materials of the β-Ga₂O₃-based crystal can be reduced, it is possible to reduce the manufacturing cost of semiconductor devices which include a β-Ga₂O₃-based crystal film and a β-Ga₂O₃-based crystal film.

EXAMPLES

In the present example, the growth rate of the β-Ga₂O₃-based crystal was evaluated using plural β-Ga₂O₃-based substrates of which main surfaces respectively have different plane orientations.

Firstly, a β-Ga₂O₃ ingot made by the FZ method was sliced using a wire saw, thereby forming β-Ga₂O₃ single crystal substrates of 1 mm in thickness. Here, five types of β-Ga₂O₃ single crystal substrates respectively having the (−201) plane, the (101) plane, the (001) plane, the (310) plane and the (010) plane as the main surface were formed as the β-Ga₂O₃-based substrate 1 while a β-Ga₂O₃ single crystal substrate having the (100) plane as the main surface was formed as Comparative Example.

Next, in the grinding and polishing process, each β-Ga₂O₃ single crystal substrate was ground and polished until the thickness became about 600 μm.

Next, each β-Ga₂O₃ single crystal substrate was subjected to organic cleaning using methanol, acetone and methanol in this order for three minutes each, running water cleaning using ultrapure water, hydrofluoric acid immersion cleaning for fifteen minutes, sulfuric acid/hydrogen peroxide mixture immersion cleaning for five minutes and running water cleaning using ultrapure water, and was further subjected to thermal cleaning under conditions of at 800° C. for ten minutes.

Next, a β-Ga₂O₃ crystal was grown on eachβ-Ga₂O₃ single crystal substrate in an oxygen-based gas atmosphere by the MBE and a β-Ga₂O₃ crystal film was thereby formed as the β-Ga₂O₃-based crystal film 20. The Ga beam-equivalent pressure was 3×10⁵ Pa.

The growth temperature and growth time of the β-Ga₂O₃ crystal were respectively 700° C. and 1 hour. In addition, on the β-Ga₂O₃ single crystal substrates having the (100) plane and the (010) plane as the main surface, crystal growth ofβ-Ga₂O₃ was also performed under the condition of a growth temperature of 500° C.

FIG. 6 is a graph showing growth rates of the respective β-Ga₂O₃ crystals on the β-Ga₂O₃ single crystal substrates.

As shown in FIG. 6, in case of crystal growth at 700° C. which is a temperature allowing a β-Ga₂O₃ crystal with sufficient quality to be grown, the growth rate was about 30 nm/hour on the β-Ga₂O₃ single crystal substrate having the (100) plane as the main surface. On the other hand, the growth rate was about 90 to 130 nm/hour on the β-Ga₂O₃ single crystal substrates having the (−201) plane, the (101) plane, the (001) plane, the (310) plane and the (010) plane as the main surface.

This result shows that, on the β-Ga₂O₃-based substrates having the (−201) plane, the (101) plane, the (001) plane, the (310) plane and the (010) plane as the main surface which were formed as the β-Ga₂O₃-based substrates 1 of the embodiments, the growth rate of the β-Ga₂O₃ crystal is remarkably faster than that on the β-Ga₂O₃ single crystal substrate having the (100) plane as the main surface. It should be noted that, it is generally rare that the growth rate of crystal is improved so much only by changing the plane orientation of the main surface of the substrate and it can be said that this result is beyond expectation of those skilled in the art.

It was also confirmed that, when the β-Ga₂O₃ crystal is grown on the β-Ga₂O₃ single crystal substrate having the (100) plane as the main surface at a growth temperature of 700° C., the growth rate is about one-fifth of that of the β-Ga₂O₃ crystal grown at a growth temperature of 500° C. It is believed that this is because the raw materials of the β-Ga₂O₃ crystal re-evaporate from the substrate.

On the other hand, it was confirmed that, when the β-Ga₂O₃ crystal is grown on the β-Ga₂O₃ single crystal substrates having the (310) plane and the (010) plane as the main surface at a growth temperature of 700° C., the growth rate is substantially the same as that of the β-Ga₂O₃ crystal grown at a growth temperature of 500° C. It is believed that re-evaporation of the raw materials of the β-Ga₂O₃ crystal from the substrate is suppressed when the β-Ga₂O₃ single crystal substrate having the (010) plane as the main surface is used. It is considered that the same applies to the case where the β-Ga₂O₃ single crystal substrates having the (−201) plane, the (101) plane and the (001) plane as the main surface are used.

FIG. 7 is a graph showing a relation between the growth rate of the β-Ga₂O₃ crystal and a rotation angle with respect to the (100) plane as the main surface of the β-Ga₂O₃ single crystal substrate. In FIG. 7, the filled square indicates a value of the growth rate at a growth temperature of 500° C. when the main surface is rotated around the c-axis. The filled circle indicates a value of the growth rate at a growth temperature of 700° C. when the main surface is rotated around the c-axis. The filled diamond indicates a value of the growth rate at a growth temperature of 700° C. when the main surface is rotated around the b-axis.

It is understood from FIG. 7 that, when the rotation angle with respect to (100) plane as the main surface of the β-Ga₂O₃ single crystal substrate is not less than 50°, the growth rate when growing the β-Ga₂O₃ crystal at a growth temperature of 700° C. is significantly improved as compared to the case where the main surface is the (100) plane. It is also understood that, when the β-Ga₂O₃ crystal is grown at a growth temperature of 500° C., the growth rate of the β-Ga₂O₃ crystal hardly depends on the rotation angle with respect to (100) plane as the main surface of the β-Ga₂O₃ single crystal substrate.

Although the embodiments and example of the invention have been described above, the invention according to claims is not to be limited to the above-mentioned embodiments and example. Further, it should be noted that all combinations of the features described in the embodiments and example are not necessary to solve the problem of the invention.

INDUSTRIAL APPLICABILITY

A crystal laminate structure in which crystals can be epitaxially grown on a β-Ga₂O₃-based substrate with high efficiency to produce a high-quality β-Ga₂O₃-based crystal film, and a method for producing the same are provided.

REFERENCE SIGNS LIST

1: β-Ga₂O₃-based substrate

2: crystal laminate structure

4: high-electron-mobility transistor

5: MESFET

6: Schottky-barrier diode

10: main surface

20: β-Ga₂O₃-based crystal film 

The invention claimed is:
 1. A crystal laminate structure, comprising: a β-Ga₂O₃-based substrate comprising as a main surface a plane rotated by not less than 50° and not more than 90° with respect to a (100) plane; and a β-Ga₂O₃-based crystal film provided on the main surface of the β-Ga₂O₃-based substrate, wherein the β-Ga₂O₃-based crystal film is in a Schottky-contact with an electrode, and wherein the β-Ga₂O₃-based substrate contains group II elements.
 2. The crystal laminate structure according to claim 1, wherein the main surface of the β-Ga₂O₃-based substrate comprises one of a (010) plane, a (001) plane, a (−201) plane, a (101) plane, and a (310) plane.
 3. The crystal laminate structure according to claim 1, wherein the β-Ga₂O₃-based substrate comprises Mg as the group II elements.
 4. The crystal laminate structure according to claim 1, wherein the β-Ga₂O₃- based crystal film comprises: an i-type β-Ga₂O₃-based crystal film provided on the main surface of the β-Ga₂O₃-based substrate; and an n-type β-(AlGa)₂O₃ crystal film provided on the i-type β-Ga₂O₃-based crystal film, and that is in the Schottky-contact with the electrode.
 5. The crystal laminate structure according to claim 4, wherein the main surface of the β-Ga₂O₃-based substrate comprises one of a (010) plane, a (001) plane, a (−201) plane, a (101) plane, and a (310) plane.
 6. The crystal laminate structure according to claim 4, wherein the β-Ga₂O₃-based substrate comprises Mg as the group II elements.
 7. The crystal laminate structure according to claim 1, wherein the β-Ga₂O₃-based crystal film comprises an n-type β-Ga₂O₃-based crystal film.
 8. The crystal laminate structure according to claim 7, wherein the main surface of the β-Ga₂O₃-based substrate comprises one of a (010) plane, a (001) plane, a (−201) plane, a (101) plane, and a (310) plane.
 9. The crystal laminate structure according to claim 7, wherein the β-Ga₂O₃-based substrate comprises Mg as the group II elements.
 10. The crystal laminate structure according to claim 1, wherein the β-Ga₂O₃-based crystal film is in an ohmic-contact with another electrode.
 11. The crystal laminate structure according to claim 1, wherein the electrode comprises a gate electrode that is in the Schottky-contact with the β-Ga₂O₃-based crystal film.
 12. The crystal laminate structure according to claim 11, further comprising a source electrode and a drain electrode each being disposed on a same surface of the crystal laminate structure that the gate electrode is disposed, each of the source electrode and the drain electrode being in an ohmic-contact with the β-Ga₂O₃-based crystal film. 